Diamond tools solutions
1.JF-01

Components: Fe Cu

Theoretical Density: 8.16g/cm3

Sintering Temperature: 830℃

Bending Strength: 1350MPa

Hardness: 98-102HRB

HApplication & Feature: Suitable for making multiple diamond tools, added as a basic powder

to lower the cost, diamond embedded well in the matrix, sharpness.

2.HYF-06

Components: Fe Cu Ni Sn

Theoretical Density: 8.05g/cm3

Sintering Temperature: 830℃

Bending Strength: 1100MPa

Hardness: 105-110HRB

Application & Formula:

Edge-grinding wheel and roller blade for processing ceramics:

(65-70)%HYF-06 + (10-20)%Fe + (10-20)%Cu + (1-2)%Sn + (3-7)%Ni + (1-2)%Ti,

Ratio of Diamond: 20-25% (25% 40/45 + 50% 50/60 + 25%60/70)

Sintering Temperature: 780℃

3.JF-26

Components: Fe Cu Ni

Theoretical Density: 8.23g/cm3

Sintering Temperature: 850℃

Bending Strength: 1400MPa

Hardness: 108-112HRB

Application & Formula:

Medium and high quality concrete high speed blade

60%JF-26 + (10-12)%Co + 15%Cu + 2%Sn + (3-5)%No(CO)4 + residue Fe

Ratio of Diamond: 25-28% (20% 40/45 + 50% 45/50 + 30%50/60)

Sintering Temperature: 850℃